This color looks pale pinkish-tan in rod form and strikes to a rich pinkish-brown. It is best to use a clear core in your bead if you are going to encase this color in clear. This color should not be worked a long time in the flame or soaked in the kiln too long, as it will turn a chalky brown tone.
|